RESUMO
Objective: To evaluate the biaxial flexural strength (BFS) of lithium disilicate (L), cemented on different substrates (epoxy resin - E and metal - M) with dual-cure resin cement (Rc) and zinc phosphate cement (Zc), not aged, thermally aged (TC) or thermo-mechanical aged (TC/MC). Material and Methods: Disks of L, E, and M were fabricated, and the cementation was performed according to the following groups: ERc (L+E+Rc); MRc (L+M+Rc); MZc (L+M+Zc); EZc (L+E+Zc). Ten samples from each described group were tested in BFS, ten more samples were subjected to TC (1×104 cycles between 5 ºC and 55 ºC water), and the last 10 samples were subjected to TC/MC (MC: 1.2×106 cycles, 50 N, 3.8 Hz). The BFS test was performed and scanning electron microscopy (SEM) was performed to evaluate the failure mode. The effect of the cementation strategy (cement/substrate) was compared in each aging method and the effect of the aging method was evaluated for each cementation strategy by one-way ANOVA and Tukey post-hoc test (α=0.05). Results: The strength values were highest to M (237.8 ~ 463.9 MPa), in comparison to the E (41.03 ~ 66.76 MPa), despite aging and luting agent. Flexural strength data decreased after TC and TC/MC in groups cemented with Zc, but was stable when cemented with Rc. SEM analysis indicated that failure origins were located at the tensile surface of the L. Conclusion: Lithium disilicate discs cemented to the metallic substrate presented the highest biaxial flexural strength. The cementation with dual-cure resin cement did not decrease BFS after aging (AU)
Objetivo: Avaliar a resistência à flexão biaxial (BFS) do dissilicato de lítio (L), cimentado sobre diferentes substratos (resina epóxi - E e metal - M) com cimento resinoso dual (Rc) e cimento de fosfato de zinco (Zc), não envelhecido, submetido ao envelhecido térmico (TC) ou ao envelhecido térmico-mecânico (TC/MC). Material e Métodos: Foram confeccionados discos de L, E e M, e a cimentação foi realizada de acordo com os seguintes grupos: ERc (L+E+Rc); MRc (L+M+Rc); MZc (L+M+Zc); EZc (L+E+Zc). Dez amostras de cada grupo descrito foram testadas em BFS, mais dez amostras foram submetidas à TC (1×104 ciclos de imersão em água entre 5 ºC e 55 ºC), e as últimas 10 amostras foram submetidas à TC/MC (MC: 1.2 ×106 ciclos, 50 N, 3.8 Hz). Foram realizados os testes de BFS e a microscopia eletrônica de varredura (MEV) para avaliar o modo de falha. O efeito da estratégia de cimentação (cimento/substrato) foi comparado em cada método de envelhecimento e o efeito do método de envelhecimento foi avaliado para cada estratégia de cimentação por ANOVA a um fator e teste post-hoc de Tukey (α=0,05). Resultados: Os valores de resistência foram maiores para M (237.8 ~ 463.9 MPa), em comparação com E (41.03 ~ 66.76 MPa), independentemente do envelhecimento e do agente cimentante utilizado. Os dados de resistência à flexão diminuíram após TC e TC/MC nos grupos cimentados com Zc, mas se mantiveram estáveis quando cimentados com Rc. A análise MEV indicou que a origem das falhas estava localizada na superfície de tração do L. Conclusão: Os discos de dissilicato de lítio cimentados ao substrato metálico apresentaram maior resistência à flexão biaxial. A cimentação com cimento resinoso dual não diminuiu o BFS após o envelhecimento (AU)
Assuntos
Envelhecimento , Cimentação , Resistência à FlexãoRESUMO
Resumo Este estudo desenvolveu e testou géis experimentais contendo íons fluoreto (F-) e estanho (Sn2+) para o controle da erosão dentária. Os espécimes polidos, de esmalte e dentina, foram previamente erodidos (solução de ácido cítrico a 1%, 10 min) e alocados aleatoriamente em 5 grupos (n = 10): Placebo - gel de hidroxipropilmetilcelulose (HMC); F + Sn + HMC - 7.500 ppm F- / 15.000 ppm Sn2+; F + HMC - 7.500 ppm F-; Gel de flúor fosfato acidulado comercial (12.300 ppm F-); e Controle - sem tratamento. Após o tratamento (aplicado por 60 s), os espécimes foram submetidos a uma ciclagem de erosão-remineralização (5 min em solução de ácido cítrico a 0,3%, 60 min em saliva artificial, 4 × / dia, 20 dias). A perda de superfície (SL, em µm) foi determinada após o 5º, 10º e 20º dias de ciclagem (α = 0,05). Para o esmalte, após 5 e 10 dias, o F + Sn + HMC apresentou a menor PS, não diferindo do gel comercial. Após 20 dias, não foram encontradas diferenças entre os grupos comercial, F + HMC e F + Sn + HMC. O placebo não diferiu do controle em nenhum momento, e ambos os grupos apresentaram a maior PS, comparado aos demais grupos. Para dentina, no 5º dia , F + Sn + HMC, F + HMC e comercial não diferiram significativamente, apresentando menor PS que o grupo controle e placebo. No 10º dia, F+Sn+HMC e comercial apresentaram a menor PS comparado ao grupo controle e placebo. No 20º dia, apenas o gel comercial apresentou PS menor que o controle e o placebo. Assim, o gel experimental F + Sn + HMC foi capaz de controlar a progressão da erosão dentária.
Abstract: This study synthesized and tested experimental gels containing fluoride (F-) and stannous (Sn2+) ions for the control of dental erosion. Enamel and dentin polished specimens were eroded (1% citric acid solution, 10 min) and randomly allocated into 5 groups (n=10): Placebo - Hydroxypropyl Methylcellulose (HMC) gel; F+Sn+HMC - 7,500 ppm F- / 15,000 ppm Sn2+; F+HMC - 7,500 ppm F-; Commercial acidulated phosphate fluoride gel (12,300 ppm F-); and Control - no treatment. After treatment (applied for 60 s), specimens underwent an erosion-remineralization cycling (5 min in 0.3% citric acid solution, 60 min in artificial saliva, 4×/day, 20 days). Surface loss (SL, in µm) was determined after the 5th, 10th and 20th days of cycling (α=0.05). For enamel, after 5 and 10 days, F+Sn+HMC presented the lowest SL, which did not differ from the commercial gel. After 20 days, no differences were found between commercial, F+HMC, and F+Sn+HMC groups. Placebo did not differ from the control at any time points, and both groups presented the highest SL when compared to the other groups. For dentin, on the 5th day, F+Sn+HMC, F+HMC and commercial did not differ significantly, showing lower SL than the control and the placebo. On the 10th day, F+Sn+HMC and commercial presented the lowest SL compared to control and placebo. After 20 days, only the commercial gel showed lower SL than the control and placebo. Thus, the experimental F+Sn+HMC gel was able to control the progression of tooth erosion.
RESUMO
Aim: To evaluate the influence of lengths and different luting agents on the bond strength of fiberglass posts' adhesion to dentin.Methods: Sixty single-root bovine teeth were endodontically treated and included in polyether and acrilyc resin to simulate a periodontal ligament. These were divided into 6 groups according to the post lengths (6, 10 or 14 mm) and luting agents (self-adhesive dual resin cement U; or etch-and-rinse dual resin cement A): U6, U10, U14, A6, A19, and A14. All fiberglass posts were cemented according to manufacturer instructions. After this, mechanical aging was performed (1.2x106 cycles; 4 Hz, 90 N). The push-out specimens were then conducted (2.0 ± 0.1 mm), with the test executed in a universal machine (10 kgf at 0.5 mm/min). Data obtained were submitted to the Kruskal-Wallis and Dunn's test. Results: No statistically significant difference was observed in bond strength between the groups due to the type of luting agent (p > 0.05). However, the isolated post-length factor showed significantly different results for the U groups (p < 0.05). The U10 group showed similar union values to U6 but statistically inferior to U14. Conclusion: bond strength of fiberglass posts of the same length as the dentin presented no differences according to the luting agent, but the post-length property influenced the bond strength when self-adhesive resin cement was used.
Objetivo: avaliar a influência dos agentes cimentantes e dos diferentes comprimentos de pinos na resistência de união de pinos de fibra de vidro a dentina. Métodos: Sessenta dentes bovinos uniradiculares tiveram a raiz endodonticamente tratada, e foram incluídos em poliéter e resina acrílica para simular o ligamento periodontal. Os espécimes foram divididos em seis grupos de acordo com o comprimento dos pinos (6, 10 ou 14mm) e dos agentes de cimentantes (cimento resinoso dual autoadesivo (RelyX U200, 3M ESPE) - U; ou cimento resinoso dual convencional (AllCem Core, FGM) - A: U6, U10, U14, A6, A19 e A14. Todos os pinos de fibra de vidro foram cimentados conforme as recomendações do fabricante. Após, o envelhecimento mecânico (1,2x106 ciclos; 4 Hz, 90 N) as amostras foram fatiadas para o teste de push-out (2,0 ± 0,1 mm) executado em uma máquina de ensaio universal (10 kgf a 0,5 mm/min). Os dados foram submetidos ao teste de Kruskal-Wallis e Dunn. Resultados: não houve diferença estatística na resistência de união entre os grupos devido ao tipo de agente cimentante (p > 0,05), mas houve para o comprimento dos pinos dos grupos U (p < 0,05). O grupo U10 apresentou valores de união semelhantes a U6, mas estatisticamente inferiores ao U14. Conclusão: a resistência de união dos pinos de fibra de vidro de um mesmo comprimento não apresentou diferenças mesmo quando cimentados com cimentos diferentes, mas o comprimento dos pinos isoladamente influenciou quando o cimento resinoso autoadesivo foi utilizado.